Standard Specification for Gray Iron Castings for Elevated Temperatures for Non-Pressure Containing Parts
Automatische name übersetzung:
Standard-Spezifikation für Grauguss für erhöhten Temperaturen für druckhaltigen Teile
NORM herausgegeben am 1.3.2011
Bezeichnung normen: ASTM A319-71(2011)
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 1.3.2011
SKU: NS-2012
Zahl der Seiten: 2
Gewicht ca.: 6 g (0.01 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Keywords:
chemical composition, elevated temperature, gray iron, iron castings, non-pressure containing, tensile strength: Grate bars, Gray iron castings--specifications, Ingot molds, Metal melting pots, Oil still furnace parts, Stoker links, Caustic pots, Elevated temperature service applications, Firebox parts, Glass molds, ICS Number Code 77.140.80 (Iron and steel castings)
1. Scope | ||
1.1 This specification covers three classes of gray iron suitable for castings exposed to temperatures encountered in such service as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots. Note 1—This specification is general, covering cast irons normally used for the above types of service, at temperatures as high as 1400°F (760°C). It is not intended to imply that all three classes are suitable throughout this entire temperature range without regard to actual service stresses. Some are suitable for long service at the lower temperatures only, unless low stresses are involved. 1.2 The three classes of gray iron covered by this specification are as follows: 1.2.1 Class I, possessing superior resistance to thermal shock, 1.2.2 Class II, possessing average resistance to thermal shock and a moderately good tensile strength (tensile strengths above 30 000 psi (207 MPa) may be expected), and 1.2.3 Class III, possessing a higher tensile strength than either Classes I or II (tensile strengths as high as 40 000 psi (276 MPa) may be expected). 1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. |
||
2. Referenced Documents | ||
|
Wollen Sie sich sicher sein, dass Sie nur die gültigen technischen Normen verwenden?
Wir bieten Ihnen eine Lösung, die Ihnen eine Monatsübersicht über die Aktualität der von Ihnen angewandten Normen sicher stellt.
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.
Letzte Aktualisierung: 2024-11-22 (Zahl der Positionen: 2 206 568)
© Copyright 2024 NORMSERVIS s.r.o.