Standard Specification for Hot-Rolled and Cold-Finished Zirconium and Zirconium Alloy Bars, Rod, and Wire for Nuclear Application
Name übersetzen
NORM herausgegeben am 1.5.2023
Bezeichnung normen: ASTM B351/B351M-13(2023)
Ausgabedatum normen: 1.5.2023
SKU: NS-1143340
Zahl der Seiten: 7
Gewicht ca.: 21 g (0.05 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
This specification covers UNS R60001, R60802, R60804, and R60901 wrought zirconium and zirconium alloy bars, rods, and wires. All material grades covered should conform to the required chemical composition requirements. Elements that are intentionally added to the melt should be identified, analyzed and reported in the chemical analysis. The zirconium and zirconium alloys should be made from ingots produced by vacuum or plasma arc melting, vacuum electron-beam melting, a combination of the three methods, or other melting processes conventionally used for reactive metals. All processes should be performed in furnaces specifically for reactive metals. Mill products included in this specification should be formed with conventional extrusion, forging, or rolling equipment that is used in primary ferrous and nonferrous plants. The cold worked and annealed materials should be in fully annealed condition unless otherwise specified. Hot worked shapes should be furnished in not descaled, mechanically descaled, or mechanically descaled and pickled finish, while cold-worked shapes should be furnished in cold-worked, ground, or pickled finish.
Keywords:
(metal), (metal) alloy, (metal) bar, (metal) rod, (metal) wire, (metal) (nuclear applications),, ICS Number Code 77.140.60 (Steel bars and rods),77.140.65 (Steel wire, wir ropes and link chains)
1. Scope | ||||||||||||||
1.1?This specification covers four grades of wrought zirconium and zirconium alloy bars, rod, and wire as follows: 1.1.1?R60001Unalloyed grade, 1.1.2?R60802Zirconium-Tin alloy (Zircaloy 2), 1.1.3?R60804Zirconium-Tin alloy (Zircaloy 4), and 1.1.4?R60901Zirconium-Niobium alloy. 1.2?Unless a single unit is used, for example corrosion mass gain in mg/dm2, the values stated in either inch-pound or SI units are to be regarded separately as standard. The values stated in each system are not exact equivalents; therefore each system must be used independently of the other. SI values cannot be mixed with inch-pound values. 1.3?The following precautionary caveat pertains only to the test method portions of this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||||||||
2. Referenced Documents | ||||||||||||||
|
Wollen Sie sich sicher sein, dass Sie nur die gültigen technischen Normen verwenden?
Wir bieten Ihnen eine Lösung, die Ihnen eine Monatsübersicht über die Aktualität der von Ihnen angewandten Normen sicher stellt.
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.
Letzte Aktualisierung: 2024-12-22 (Zahl der Positionen: 2 217 000)
© Copyright 2024 NORMSERVIS s.r.o.