ASTM D1683/D1683M-22

5.1?The manufacturing of textile products uses seam engineering to determine the best combination of sewing thread, stitch type, seam type, and stitch density to construct the end use structure. These four seam engineering variables contribute to a textile product being able to achieve the maximum sewn seam strength performance and structural integrity when cut pieces of fabric are joined together.

5.2?This test method can be used to determine the sewn seam strength and sewn seam efficiency of critical sewn seam assemblies with each fabric. Because sewn seam strength and sewn seam efficiency varies with each fabric, both of the standard seam assemblies, noted in Table 1, should be used when comparing the seam strength of different fabrics. Table 1 lists the default seam assembly specifications to be used for fabrics made with low, medium and high density yarn counts. If a determination cannot be made as to which seam is the best suited for a particular fabric, all should be evaluated.

5.3?Seams prepared for this test method should be made by competent factory sewing operators familiar with the potential for damage to the integrity of the sewn seam when stitching is improperly done.

5.4?This test method is applicable whenever a determination of sewn seam strength is required. The breaking force of the seam and fabric will permit estimation of seam efficiency. This test method can be used as an aid for estimating seam strength for any given fabric.

5.5?Seam engineering techniques for specific fabric types can also be determined by utilizing this test method.

5.6?This test method can be used to determine when the sewn seam is affected by seam slippage. While the ultimate consequence of this phenomenon is rupture, seam slippage greater than either the values stated in customer specifications, or as agreed upon by purchaser/supplier may severely reduce the integrity such that the product cannot be used for its intended purpose.

1.1?This test method measures the sewn seam strength in woven fabrics by applying a force perpendicular to the sewn seams.

1.2?This test method is used when the maximum breaking force measurement to rupture of a woven fabric sewn seam is required.

1.3?This test method does not predict actual wear performance of a seam.

1.4?The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

1.5?This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.6?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.