Standard Test Method for Open-Hole Tensile Strength of Polymer Matrix Composite Laminates
Automatische name übersetzung:
Standard Test Method for Open-Loch Zugfestigkeit von Polymermatrix-Verbundschichtstoffe
NORM herausgegeben am 1.1.2011
Bezeichnung normen: ASTM D5766/D5766M-11
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 1.1.2011
SKU: NS-32450
Zahl der Seiten: 7
Gewicht ca.: 21 g (0.05 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Keywords:
composite materials, open-hole tensile strength, tension testing, Composites, Laminates, Open hole tensile strength, Tensile properties/testing, ICS Number Code 83.120 (Reinforced plastics)
Significance and Use | ||||||||||||||||||||||||||||
This test method is designed to produce notched tensile strength data for structural design allowables, material specifications, research and development, and quality assurance. Factors that influence the notched tensile strength and should therefore be reported include the following: material, methods of material fabrication, accuracy of lay-up, laminate stacking sequence and overall thickness, specimen geometry (including hole diameter, diameter-to-thickness ratio, and width-to-diameter ratio), specimen preparation (especially of the hole), specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and volume percent reinforcement. Properties that may be derived from this test method include the following: Open-hole (notched) tensile strength (OHT). |
||||||||||||||||||||||||||||
1. Scope | ||||||||||||||||||||||||||||
1.1 This test method determines the open-hole tensile strength of multidirectional polymer matrix composite laminates reinforced by high-modulus fibers. The composite material forms are limited to continuous-fiber or discontinuous-fiber (tape or fabric, or both) reinforced composites in which the laminate is balanced and symmetric with respect to the test direction. The range of acceptable test laminates and thicknesses are described in 8.2.1. 1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. 1.2.1 Within the text the inch-pound units are shown in brackets. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||||||||||||||||||||||||||
2. Referenced Documents | ||||||||||||||||||||||||||||
|
Historisch
1.10.2011
Historisch
1.5.2012
Historisch
1.12.2012
Historisch
1.9.2009
Historisch
1.3.2008
Historisch
1.5.2008
Wollen Sie sich sicher sein, dass Sie nur die gültigen technischen Normen verwenden?
Wir bieten Ihnen eine Lösung, die Ihnen eine Monatsübersicht über die Aktualität der von Ihnen angewandten Normen sicher stellt.
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.
Letzte Aktualisierung: 2024-11-22 (Zahl der Positionen: 2 206 568)
© Copyright 2024 NORMSERVIS s.r.o.