Standard Practice for Assessing the Tendency of Industrial Boiler Waters to Cause Embrittlement (USBM Embrittlement Detector Method)
Automatische name übersetzung:
Standard Praxis zur Beurteilung der Tendenz zum Industriekessel Waters zu Versprödung führen (USBM Versprödung Detector-Methode)
NORM herausgegeben am 1.1.2014
Bezeichnung normen: ASTM D807-14
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 1.1.2014
SKU: NS-39352
Zahl der Seiten: 6
Gewicht ca.: 18 g (0.04 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Keywords:
boiler water, cracking, detector, embrittlement, intercrystalline, ICS Number Code 27.060.30 (Boilers and heat exchangers)
Significance and Use | ||||||||||||||
5.1 Embrittlement is a form of intercrystalline cracking that is associated with the exposure of boiler steel to a combination of physical and chemical factors. For embrittlement of boiler metal to occur, the metal must be under stress, it must be at the site of a leak, and it must be exposed to the concentrated boiler water. In addition, the boiler water must be embrittling in nature. The precise chemical causes of the embrittling nature of some waters are not well understood. Experience has shown that certain waters exhibit an embrittling characteristic while others do not. 5.2 Because embrittlement is a form of cracking, it is nearly impossible to detect in an operating boiler until a failure has occurred. In general, cracking failures tend to be sudden, and often with serious consequences. This practice offers a way to determine whether a particular water is embrittling or not. It also makes it possible to determine if specific treatment actions have rendered the water nonembrittling. |
||||||||||||||
1. Scope | ||||||||||||||
1.1 This practice,3 known as the embrittlement-detector method, covers the apparatus and procedure for determining the embrittling or nonembrittling characteristics of the water in an operating boiler. The interpretation of the results shall be restricted to the limits set forth in 8.6. 1.2 The effectiveness of treatment
to prevent cracking, as well as an indication of whether an unsafe
condition exists, are shown by this practice. Such treatments are
evaluated in terms of method specimen resistance to failure.
1.3 The practice may be applied to embrittlement resistance testing of steels other than boiler plate, provided that a duplicate, unexposed specimen does not crack when bent 90° on a 2-in. (51-mm) radius. 1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||||||||||||
2. Referenced Documents | ||||||||||||||
|
Historisch
1.3.2012
Historisch
1.4.2010
Historisch
1.12.2011
Historisch
1.6.2010
Historisch
1.3.2013
Wollen Sie sich sicher sein, dass Sie nur die gültigen technischen Normen verwenden?
Wir bieten Ihnen eine Lösung, die Ihnen eine Monatsübersicht über die Aktualität der von Ihnen angewandten Normen sicher stellt.
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.
Letzte Aktualisierung: 2024-09-28 (Zahl der Positionen: 2 350 600)
© Copyright 2024 NORMSERVIS s.r.o.