Standard Test Methods for Rubber Properties in Compression or Shear (Mechanical Oscillograph)
Automatische name übersetzung:
Standard-Prüfverfahren für Gummi Eigenschaften in Kompression oder Shear (Mechanical Oscillograph )
NORM herausgegeben am 1.7.2006
Bezeichnung normen: ASTM D945-06
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 1.7.2006
SKU: NS-39857
Zahl der Seiten: 11
Gewicht ca.: 33 g (0.07 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Keywords:
chronograph, compression, creep, deflection, deformation, dynamic modulus, elevated temperature, hysterisis, initial creep, kinetic energy, low temperature, mechanical oscillograph, point modulus, resilience, set, shear, static modulus, strain, stress, subnormal temperature, tangent modulus, Yerzley
Significance and Use | ||||||||
The rubber properties that are measurable by these test methods are important for the isolation and absorption of shock and vibration. These properties may be used for quality control, development and research. Measurements in compression are influenced by specimen shape. This shape factor may be described as the ratio of the loaded surface area to the unloaded surface area. In applying data from a compression specimen, shape factor must be incorporated into the mathematical transferal to the application. |
||||||||
1. Scope | ||||||||
1.1 These test methods cover the use of the Yerzley mechanical oscillograph for measuring mechanical properties of rubber vulcanizates in the generally small range of deformation that characterizes many technical applications. These properties include resilience, dynamic modulus, static modulus, kinetic energy, creep, and set under a given force. Measurements in compression and shear are described., 1.2 The test is applicable primarily, but not exclusively, to materials having static moduli at the test temperature such that forces below 2 MPa (280 psi) in compression or 1 MPa (140 psi) in shear will produce 20 % deformation, and having resilience such that at least three complete cycles are produced when obtaining the damped oscillatory curve. The range may be extended, however, by use of supplementary masses and refined methods of analysis. Materials may be compared either under comparable mean stress or mean strain conditions. 1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For a specific warning see . |
||||||||
2. Referenced Documents | ||||||||
|
Wollen Sie sich sicher sein, dass Sie nur die gültigen technischen Normen verwenden?
Wir bieten Ihnen eine Lösung, die Ihnen eine Monatsübersicht über die Aktualität der von Ihnen angewandten Normen sicher stellt.
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.
Letzte Aktualisierung: 2024-09-12 (Zahl der Positionen: 2 346 316)
© Copyright 2024 NORMSERVIS s.r.o.