ASTM E1641-13

5.1 Thermogravimetry provides a rapid method for determining the temperature-decomposition profile of a material.

5.2 This test method can be used for estimating lifetimes of materials, using Test Method E1877 provided that a relationship has been established between the thermal endurance test results and actual lifetime tests.

1.1 This test method describes the determination of the kinetic parameters, Arrhenius activation energy, and preexponential factor by thermogravimetry, based on the assumption that the decomposition obeys first-order kineticsusing the Ozawa/Flynn/Wall isoconversional method (1).²

1.2 This test method is generally applicable to materials with well-defined decomposition profiles, namely, a smooth, continuous mass change with a single maximum rate.

1.3 This test method is normally applicable to decomposition occurring in the range from 400 to 1300K (nominally 100 to 1000°C). The temperature range may be extended depending on the instrumentation used.

1.4 This method is similar to ISO 11358-2 but differs in its mathematical treatment.

1.5 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.