Standard Test Method for Measurement of Hydrogen Embrittlement Threshold in Steel by the Incremental Step Loading Technique
Automatische name übersetzung:
Standard Test Method for Messung der Wasserstoffversprödung Threshold in Stahl durch die Incremental-Step-Loading-Technik
NORM herausgegeben am 1.8.2012
Bezeichnung normen: ASTM F1624-12
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 1.8.2012
SKU: NS-50952
Zahl der Seiten: 12
Gewicht ca.: 36 g (0.08 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Keywords:
decreasing loading rate, delayed brittle failure, displacement control, fasteners, hydrogen embrittlement threshold, hydrogen induced stress cracking, rising step load, slow strain rate, ICS Number Code 77.040.10 (Mechanical testing of metals)
Significance and Use | ||||||||||||||||||||||||||||||||||
5.1 This test method is used for research, design, service evaluation, manufacturing control, and development. This test method quantitatively measures stress parameters that are used in a design or failure analysis that takes into account the effects of environmental exposure including that which occurs during processing, such as plating (8) (ASTM STP 962). 5.2 For plating processes, the value of σ 5.3 For quality control purposes, an accelerated test is devised that uses a specified loading rate, which is equal to or lower than the loading rate necessary to determine the threshold stress (see 8.1). 5.4 For fasteners, the value of σ5.5 For fasteners, the value of σ5.6 To measure the relative susceptibility of steels to hydrogen pickup from various fabrication processes, a single, selected, discriminating rate is used to rank the resistance of various materials to hydrogen embrittlement. 5.7 Annex A1 describes the application of this standard test method to hydrogen embrittlement testing of fasteners. |
||||||||||||||||||||||||||||||||||
1. Scope | ||||||||||||||||||||||||||||||||||
1.1 This test method establishes a procedure to measure the susceptibility of steel to a time-delayed failure such as that caused by hydrogen. It does so by measuring the threshold for the onset of subcritical crack growth using standard fracture mechanics specimens, irregular-shaped specimens such as notched round bars, or actual product such as fasteners 1.2 This test method is used to evaluate quantitatively: 1.2.1 The relative susceptibility of steels of different composition or a steel with different heat treatments; 1.2.2 The effect of residual hydrogen in the steel as a result of processing, such as melting, thermal mechanical working, surface treatments, coatings, and electroplating; 1.2.3 The effect of hydrogen introduced into the steel caused by external environmental sources of hydrogen, such as fluids and cleaners maintenance chemicals, petrochemical products, and galvanic coupling in an aqueous environment. 1.3 The test is performed either in air, to measure the effect if residual hydrogen is in the steel because of the processing (IHE), or in a controlled environment, to measure the effect of hydrogen introduced into the steel as a result of the external sources of hydrogen (EHE) as detailed in ASTM STP 543. 1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.5 This standard does not
purport to address all of the safety concerns, if any, associated
with its use. It is the responsibility of the user of this standard
to establish appropriate safety and health practices and determine
the applicability of regulatory limitations prior to use.
|
||||||||||||||||||||||||||||||||||
2. Referenced Documents | ||||||||||||||||||||||||||||||||||
|
Historisch
15.5.2014
Historisch
15.5.2014
Historisch
1.3.2012
Historisch
1.11.2008
Historisch
15.11.2012
Historisch
1.8.2013
Bereitstellung von aktuellen Informationen über legislative Vorschriften in der Sammlung der Gesetze bis zum Jahr 1945.
Aktualisierung 2x pro Monat!
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.
Letzte Aktualisierung: 2024-11-22 (Zahl der Positionen: 2 206 568)
© Copyright 2024 NORMSERVIS s.r.o.