Standard Practice for Nondestructive Pull Testing of Wire Bonds
Automatische name übersetzung:
Standard Praxis für die zerstörungsfreie Prüfung von Pull Drahtverbindungen
NORM herausgegeben am 1.1.2001
Bezeichnung normen: ASTM F458-84(2001)
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 1.1.2001
SKU: NS-55376
Zahl der Seiten: 3
Gewicht ca.: 9 g (0.02 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Keywords:
nondestructive testing of individual wire bonds, ultrasonic, thermal compression, thermosonic, wire bonds, pull test, bonding, ICS Number Code 29.120.20 (Connecting devices)
1. Scope | ||||
1.1 This practice covers nondestructive testing of individual wire bonds made by either ultrasonic, thermal compression or thermosonic techniques. The test is destructive to nonacceptable wire bonds but is designed to avoid damage to acceptable wire bonds. Note 1--Common usage at the present time considers the term "wire bond" to include the entire interconnection: both welds and the intervening wire span. 1.2 The practice covers wire bonds made with small-diameter (from 0.0007 to 0.003-in. (18 to 76-m)) wire of the type used in integrated circuits and hybrid microcircuits. 1.3 This practice can be used only when the loop height of the wire bond is large enough to allow a suitable hook for pulling to be placed under the wire. 1.4 While the procedure is applicable to wire of any composition and metallurgical state, criteria are given only for gold and aluminum wire. 1.5 A destructive pull test is used on wire bonds of the same type and geometry to provide the basis for the determination of the nondestructive pulling force to be used in this practice. This may only be used if the sample standard deviation, s, of the pulling forces required to destroy at least 25 of the same wire bonds tested by the destructive pull-test method is less than or equal to 0.25 of the sample average, x. If s > 0.25 x, this practice may not be used. Note 2--If s > 0.25 x, some aspect of the bonding process is out of control. Following corrective action, the destructive pull-test measurements should be repeated to determine if the s 0.25 xcriterion is met. 1.6 The nondestructive wire-bond pull test is to be performed before any other treatment or screening following bonding and at the same point in processing as the accompanying destructive test. Preferably, this is done immediately after bonding. 1.7 The procedure does not ensure against wire-bond failure modes induced after the test has been performed. 1.8 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only. 1.9 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
||||
2. Referenced Documents | ||||
|
Bereitstellung von aktuellen Informationen über legislative Vorschriften in der Sammlung der Gesetze bis zum Jahr 1945.
Aktualisierung 2x pro Monat!
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.
Letzte Aktualisierung: 2024-10-31 (Zahl der Positionen: 2 208 647)
© Copyright 2024 NORMSERVIS s.r.o.