Standard Test Method for Ranking Resistance of Plastic Materials to Sliding Wear Using a Block-On-Ring Configuration
Name übersetzen
NORM herausgegeben am 1.11.2017
Bezeichnung normen: ASTM G137-97(2017)
Anmerkung: UNGÜLTIG
Ausgabedatum normen: 1.11.2017
SKU: NS-802855
Zahl der Seiten: 7
Gewicht ca.: 21 g (0.05 Pfund)
Land: Amerikanische technische Norm
Kategorie: Technische Normen ASTM
Keywords:
block-on-ring, friction, plastics, wear,, ICS Number Code 19.060 (Mechanical testing),83.140.01 (Rubber and plastic products in general)
Significance and Use | ||||||||||||
5.1 The specific wear rates determined by this test method can be used as a guide in ranking the wear resistance of plastic materials. The specific wear rate is not a material property and will therefore differ with test conditions and test geometries. The significance of this test will depend on the relative similarity to the actual service conditions. 5.2 This test method seeks only to describe the general test procedure and the procedure for calculating and reporting data. Note 2: This test configuration allows steady state specific
wear rates to be achieved very quickly through the use of high
loads and speeds. The thrust washer configuration described in Test
Method D3702 does not allow
for the use of such high speeds and loads because of possible
overheating (which may cause degradation or melting, or both) of
the specimen. Despite the differences in testing configurations, a
good correlation in the ranking of wear resistance is achieved
between the two tests (Table
X2.1).
|
||||||||||||
1. Scope | ||||||||||||
1.1 This test method covers a laboratory procedure to measure the resistance of plastic materials under dry sliding conditions. The test utilizes a block-on-ring geometry to rank materials according to their sliding wear characteristics under various conditions. 1.2 The test specimens are small so that they can be molded or cut from fabricated plastic parts. The test may be run at the load, velocity, and temperature which simulate the service condition. 1.3 Wear test results are reported as specific wear rates calculated from volume loss, sliding distance, and load. Materials with superior wear resistance have lower specific wear rates. 1.4 This test method allows the use of both single- and multi-station apparatus to determine the specific wear rates. 1.5 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only. 1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||||||
2. Referenced Documents | ||||||||||||
|
Wollen Sie sich sicher sein, dass Sie nur die gültigen technischen Normen verwenden?
Wir bieten Ihnen eine Lösung, die Ihnen eine Monatsübersicht über die Aktualität der von Ihnen angewandten Normen sicher stellt.
Brauchen Sie mehr Informationen? Sehen Sie sich diese Seite an.
Letzte Aktualisierung: 2024-11-01 (Zahl der Positionen: 2 208 817)
© Copyright 2024 NORMSERVIS s.r.o.